| 35% Glass Reinforced, Heat Stabilized, Polyamide 6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.41 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.20 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 5.8 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.8 | -- | % | |
| Viscosity Number | 140 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11000 | 6500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 190 | 115 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.2 | 5.0 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 11 | 12 | kJ/m² | |
| -30°C | 10 | 10 | kJ/m² | |
| 23°C | 16 | 22 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 90 | 90 | kJ/m² | |
| 23°C | 90 | 90 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 13 | 20 | kJ/m² | ISO 180/1A |
| Multi-Axial Instrumented Impact Energy (23°C) | 3.00 | 6.00 | J | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 208 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 215 | -- | °C | ISO 306/B50 |
| Melting Temperature 1 | 221 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 1.1E-4 | -- | cm/cm/°C |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flammability Classification (1.50 mm) | HB | -- | IEC 60695-11-10, -20 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® STAMAX 20YM240 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® STAMAX |
| Sylvin 8215-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ADEKA EP-4100G | Adeka Corporation | Epoxy | ADEKA |
| K PP 11000 | Technovinyl Polymers India Ltd. | TPO | K PP |
| Lumid® HI3232A(W) | LG Chem Ltd. | Nylon 6 | Lumid® |