Borealis PP MB250WG
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oZPgvD_Borealis-PP-MB250WG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MB250WG is a 20 % mineral filled polypropylene compound intended for injection moulding. Applications MB250WG has been developed especially for the white goods industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 30.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2500 | MPa | ISO 178 |
| Flexural Stress | 40.0 | MPa | ISO 178 |
| Flexural Strain | 5.0 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 85 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 110 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 83.0 | °C | ISO 306/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 40.0 - 80.0 | °C | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Back Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100-200 mm/s |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL NY6-IM1 | Polymer Resources Ltd. | Nylon 6 | PRL |
| Styrolution PS 5801 | INEOS Styrolution Group GmbH | PS (HIPS) | Styrolution PS |
| HIDEN® U090 | YUHWA Korea Petrochemical Ind. Co., Ltd. | UHMWPE | HIDEN® |
| Leona™ 14G15 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| LNP™ THERMOCOMP™ EC008PXQ compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |