ALAMID® 6.6 MOD UNGEFARBT-8300
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LEIS Polytechnik - polymere Werkstoffe GmbH |
| Trademark: | ALAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oYgiLT_ALAMID-6-6-MOD-UNGEFARBT-8300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| polyamide 6.6 + 15% carbon fibres, modified |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | 0.20 to 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ISO 527-2 |
| Tensile Stress | 85.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Coefficient of Friction (vs. Steel - Dynamic) | 0.10 to 0.19 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 25 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) 2 | 260 | °C | ISO 3146 |
| CLTE 3 | ISO 11359-2 | ||
| Flow : 23 to 85°C | 1.3E-5 | cm/cm/°C | |
| Transverse : 23 to 85°C | 2.7E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | 60mm x 60mm x 2mm |
| 2 . | 10K/min |
| 3 . | 60mm x 60mm x 2mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 202F | RTP Company | Nylon 12 | RTP |
| TECOLITE KM-30B(J) | KYOCERA Chemical Corporation | Phenolic | TECOLITE |
| TIPPLEN® R 359 | MOL Petrochemicals Co. Ltd. | PP Random Copolymer | TIPPLEN® |
| Altuglas® BS 130 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| LNP™ LUBRICOMP™ OFL36A compound | SABIC Innovative Plastics | PPS | LNP™ LUBRICOMP™ |