Lustran® 308 NR
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Lustran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oY4C5A_Lustran308NR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lustran® 308 resin is a low gloss, easy-flowing grade of ABS (acrylonitrile butadiene styrene). FEATURES
APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 21 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2210 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 36.2 | MPa | ASTM D638 |
| Flexural Modulus | 2450 | MPa | ASTM D790 |
| Flexural Strength | 72.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 170 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 88.9 | °C | ASTM D648 |
| 0.45 MPa, annealed | 100 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 75.6 | °C | ASTM D648 |
| 1.8 MPa, annealed | 95.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 106 | °C | ASTM D1525 1 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 218 - 260 | °C | |
| Mold Temperature | 29 - 60 | °C |
| Note Message | |
|---|---|
| 1 . | 标准 B (120°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 H FR | RTP Company | Nylon 66 | RTP |
| Elvax® 240A | DuPont Packaging & Industrial Polymers | EVA | Elvax® |
| Hanwha Total PE F120A | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | HDPE | Hanwha Total PE |
| Latilub 66-15T G/30 | LATI S.p.A. | Nylon 66 | Latilub |
| Auracell® CAP MH | Rotuba Extruders, Inc. | CAP | Auracell® |