SITRALIN 15E-TF15-HK-GS5 / black
| Category: | ASA+Nylon , Acrylonitrile Styrene Acrylate + Nylon |
| Manufacturer: | SITRAPLAS GmbH |
| Trademark: | SITRALIN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oXyNGy_SITRALIN-15E-TF15-HK-GS5-black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 16.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | 0.20 to 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield | 45.0 | MPa | ISO 527-2/50 |
| Break | 40.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break | 15 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 108 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 60 x 60 x 2 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203 TFE 10 | RTP Company | Nylon 66 | RTP |
| NORYL™ WCV065 resin | SABIC Innovative Plastics | PPE+Polyolefin | NORYL™ |
| EPLAMID 6 GI0 15 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 6 | EPLAMID 6 |
| HiFill® PBT FR-DE | Techmer Engineered Solutions | PBT | HiFill® |
| Karina WHITE PVC COMPOUND 105850-10/174-B-ISE-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |