LNP™ THERMOCOMP™ DF0046P compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oXoFUB_LNPTHERMOCOMPDF0046Pcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP DF0046P is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Exceptional Processing, Flame Retardant, Non-Brominated & Non-Chlorinated Flame Retardant. Also known as: LNP* THERMOCOMP* Compound DF-1004 EP FR ECO Product reorder name: DF0046P |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.20 - 0.40 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.30 - 0.50 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.40 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6160 | MPa | ASTM D638 |
| -- | 6930 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 95.1 | MPa | ASTM D638 |
| Fracture | 97.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 3.6 | % | ASTM D638 |
| Fracture | 3.3 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 5980 | MPa | ASTM D790 |
| -- | 6560 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 138 | MPa | ASTM D790 |
| -- | 151 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 75 | J/m | ASTM D256 |
| 23°C 2 | 8.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 470 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 10.5 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 141 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 137 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 3 | 138 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 4.7E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 2.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 1.1E-4 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S RV300K 333 NER | Radici Plastics | Nylon 6 | Radilon® |
| Sylvin 6417-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Bormed™ RJ880MO | Borealis AG | PP Random Copolymer | Bormed™ |
| Andur 7003 AP-M | Anderson Development Company | PUR-Ether/TDI | Andur |
| Geon™ BIO RC8000 | PolyOne Corporation | PVC, Flexible | Geon™ BIO |