Generic VLDPE
| Category: | VLDPE , Very Low Density Polyethylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oXZbZH_Generic-VLDPE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic VLDPE This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.884 to 0.905 | g/cm³ | ASTM D792 |
| 23°C | 0.900 to 0.911 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 0.74 to 2.5 | g/10 min | ASTM D1238 |
| 190°C/2.16 kg | 0.80 to 13 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 79 to 94 | ASTM D2240 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 49.0 to 100 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| Yield, 23°C | 5.00 to 7.00 | MPa | |
| Break, 23°C | 30.6 to 32.4 | MPa | |
| Tensile Elongation (Break, 23°C) | 490 to 800 | % | ISO 527-3 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.7 to -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 38.0 to 88.0 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 110 to 120 | °C | |
| -- | 114 to 119 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 26 to 84 | ASTM D2457 | |
| Haze | 1.5 to 30 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADDINYL A2 X | ADDIPLAST | Nylon 66 | ADDINYL |
| apilon 52® DE 55 | API SpA | TPU-Polyester | apilon 52® |
| Fainplast PVC GSK 88 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| OTECH ALLOY OM5130-Boot | OTECH Corporation | TP, Unspecified | OTECH ALLOY |
| SCHULABLEND® (PA/PP) M/MO 5101 | A. Schulman Europe | Nylon+PP | SCHULABLEND® |