Durethan® AKV 25 FN 00 000000
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oXX4ub_DurethanAKV25FN00000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, 25 % glass, injection molding, halogen free flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.39 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (270°C/2.16 kg) | 12.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 270°C, 2.00mm 1 | 0.90 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.10 | -- | % | ISO 2577 |
| Flow direction : 270°C, 2.00mm 3 | 0.30 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.10 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 4.6 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.5 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9600 | 5800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 125 | 80.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | 6.0 | % | ISO 527-2/5 |
| Nominal Tensile Strain at Break (23°C) | 3.4 | -- | % | ISO 527-2/50 |
| Flexural Modulus 5(23°C) | 9100 | 5700 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% strain, 23°C | -- | 120 | MPa | ISO 178/A |
| 23°C 6 | 210 | 135 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 3.3 | 5.8 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 66, GFHR, 14-100, GF25 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.070 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 60 | 60 | kJ/m² | ISO 179/1eU |
| 23°C | 60 | 65 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | < 10 | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 55 | 65 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 225 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 225 | -- | °C | ISO 306/B120 |
| Ball Pressure Test (228°C) | Pass | -- | IEC 60695-10-2 | |
| Melting Temperature 8 | 260 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.1E+16 | -- | ohms | IEC 60167 |
| Volume Resistivity (23°C) | 7.4E+15 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C, 1.00 mm) | 35 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (CTI) | PLC 0 | -- | UL 746 | |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.400 mm | V-0 | -- | UL 94 | |
| 0.750 mm | V-0 | -- | UL 94 | |
| 1.50 mm | V-0 | -- | UL 94 | |
| 3.00 mm | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.400 mm | 960 | -- | °C | IEC 60695-2-12 |
| 0.800 mm | 960 | -- | °C | IEC 60695-2-12 |
| 1.50 mm | 960 | -- | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.400 mm | 775 | -- | °C | IEC 60695-2-13 |
| 0.750 mm | 775 | -- | °C | IEC 60695-2-13 |
| 1.50 mm | 775 | -- | °C | IEC 60695-2-13 |
| 3.00 mm | 775 | -- | °C | IEC 60695-2-13 |
| Oxygen Index 9 | 38 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 265 - 285 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 120°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 120°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| 9 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mowital® B 20 H | Kuraray Co., Ltd. | PVB | Mowital® |
| TOYOBO Urethane A3064D | TOYOBO America, Inc. | PUR-Ether | TOYOBO Urethane |
| Karina PVC COMPOUND E-75853-35/1-BY-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hostacom TRC 411N C11515 | LyondellBasell Industries | PP, Unspecified | Hostacom |
| ULTEM™ 1010F resin | SABIC Innovative Plastics | PEI | ULTEM™ |