MarFlex® HHM TR-130
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | MarFlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oXSysf_MarFlex-HHM-TR-130.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MarFlex® HHM TR-130 is a High Density Polyethylene material. It is available in Latin America or North America for blown film. Important attributes of MarFlex® HHM TR-130 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.937 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.25 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 25 µm, Blown Film | 607 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 834 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 54.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 49.0 | MPa | |
| Tensile Elongation 1 | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 310 | % | |
| TD : Break, 25 µm, Blown Film | 840 | % | |
| Oxygen Transmission Rate (Wet) (25 µm, Blown Film) | 6000 | cm³/m²/24 hr | ASTM F1927 |
| Water Vapor Transmission Rate (25 µm, Blown Film) | 13 | g/m²/24 hr | ASTM F1249 |
| Dart Drop Test - Blown Film (25.4 µm) | 19.3 | kN/m | ASTM D1709 |
| Elmendorf Tear Strength 2 | ASTM D1922 | ||
| MD : 25.4 µm | 6.2 | kN/m | |
| TD : 25.4 µm | 617.7 | kN/m |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnamid® T- 27 MHLS | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| AKROMID® A3 GF 10 natural (2852) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| BP Flex 7500 VPL BLK | Buckeye Polymers, Inc. | TPV | BP Flex |
| CP PRYME® Acetal AC100-27 | Chase Plastics Services Inc. | Acetal (POM) Copolymer | CP PRYME® Acetal |
| Durethan® DP AKV 30 FN00 DUS013 000000 | LANXESS GmbH | Nylon 66 | Durethan® |