HiFill® PP FR 2020
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oWIyWM_HiFill-PP-FR-2020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill® PP FR 2020 is a Polypropylene Copolymer (PP Copolymer) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.960 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/1.05 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 4.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.015 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 24.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 80 | % | ASTM D638 |
| Flexural Modulus | 1030 | MPa | ASTM D790 |
| Flexural Strength | 40.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 87.8 | °C | |
| 1.8 MPa, Unannealed | 71.1 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 18 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| TPCI # | Pass | DIN 4102-B2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 216 to 238 | °C | |
| Middle Temperature | 216 to 238 | °C | |
| Front Temperature | 216 to 238 | °C | |
| Processing (Melt) Temp | 221 | °C | |
| Mold Temperature | 26.7 to 48.9 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G0 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| TAROMID A 280 Z1 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| Diakon® Rapide CLG910B | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| Hylon® N7200HL | Ravago Manufacturing Americas, LLC | Nylon 6/12 | Hylon® |
| VALOX™ ENH3500 resin | SABIC Innovative Plastics Europe | PBT | VALOX™ |