NYLOY® D-0400N
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Nytex Composites Co., Ltd. |
| Trademark: | NYLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oW4MiW_NYLOY-D-0400N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NYLOY® D-0400N is a Polycarbonate + ABS (PC+ABS) material. It is available in Asia Pacific or North America for injection molding. Primary attribute of NYLOY® D-0400N: Impact Resistant. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.977 | g/cm³ | ASTM D792 |
| -- | 1.11 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow | 0.66 | % | |
| Across Flow | 0.73 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 82 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 56.9 | MPa | ASTM D638 |
| -- | 48.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 54 | % | ASTM D638 |
| Break | 75 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2350 | MPa | ASTM D790 |
| -- | 2220 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 84.3 | MPa | ASTM D790 |
| -- | 78.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 35 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.18 mm | 270 | J/m | |
| 23°C, 3.18 mm | 570 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 125 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 94.0 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU P895RSUA | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| SLOVASTER® B GF 40 | Plastcom | PBT | SLOVASTER® |
| CompaMid® PA 6.6 GF 30 | DimeLika Plast GmbH | Nylon 66 | CompaMid® |
| DJSilicone NE-9250 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Sylvin 5145-85 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |