Toraycon® 5174G-X11
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Toray Resin Company |
| Trademark: | Toraycon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oVYwgt_Toraycon-5174G-X11.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toraycon® 5174G-X11 is a Polybutylene Terephthalate (PBT) product filled with 20% glass fiber. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.55 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 3.00 mm 1 | 0.90 | % | |
| Flow : 3.00 mm 2 | 0.40 | % | |
| Water Absorption (23°C, 24 hr) | 0.070 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6600 | MPa | ISO 527-2 |
| Tensile Stress (23°C) | 95.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.1 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 6300 | MPa | ISO 178 |
| Flexural Stress (23°C) | 150 | MPa | ISO 178 |
| Coefficient of Friction 3 | 0.20 | ||
| Coefficient of Friction - vs. Metal 4 | 0.160 | Suzuki Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bar Flow Length 5(250°C, 1.00 mm) | 113 | mm | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 57 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 207 | °C | ISO 75-2/A |
| CLTE - Flow (-30 to 100°C) | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant 6 | IEC 60250 | ||
| 23°C, 50 Hz | 3.80 | ||
| 23°C, 1 kHz | 3.80 | ||
| Dissipation Factor 7 | IEC 60250 | ||
| 23°C, 50 Hz | 2.0E-3 | ||
| 23°C, 1 MHz | 0.020 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | vs. Metal |
| 4 . | Without Lubrication |
| 5 . | 93 MPa |
| 6 . | 60% RH |
| 7 . | 60% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Teflon® PFA 440HPA | DuPont Fluoropolymers | PFA | Teflon® PFA |
| NEXUS PC/PET PC/PET7901 | Nexus Resin Group, LLC. | PC+PET | NEXUS PC/PET |
| IPC PP 4810H-T | International Polymers Corporation | PP Homopolymer | IPC PP |
| Hostacom TRC 333N G72862 | LyondellBasell Industries | PP Copolymer | Hostacom |
| UNITIKA Nylon 6 M1030E | UNITIKA Plastics Division | Nylon 6 | UNITIKA Nylon 6 |