Hytrel® HTR237BG BK320
| Category: | TPC-ET , THERMOPLASTIC POLYESTER ELASTOMER |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Hytrel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oV6lqE_Hytrel-HTR237BG-BK320.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 45 Shore D, Lubricated, High Viscosity Polyester Elastomer Developed for Blow Molding |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/2.16 kg) | 0.40 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 4.00 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 45 | ||
| Shore D, 15 sec | 41 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 90.0 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Break | 30.0 | MPa | |
| 10% Strain | 7.60 | MPa | |
| 50% Strain | 12.1 | MPa | |
| 100% Strain | 15.0 | MPa | |
| 300% Strain | 26.0 | MPa | |
| Tensile Strain (Break) | > 300 | % | ISO 527-2 |
| Flexural Modulus | 90.0 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ISO 34-1 | ||
| Across Flow | 120 | kN/m | |
| Flow | 120 | kN/m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C, Partial Break | 120 | kJ/m² | |
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 57.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 41.0 | °C | ISO 75-2/A |
| Brittleness Temperature | -100 | °C | ISO 974 |
| Glass Transition Temperature 1 | -45.0 | °C | ISO 11357-2 |
| Melting Temperature 2 | 204 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moldex® QS254D/QCM240 | Mitsubishi Chemical Corporation | Polyolefin, Unspecified | Moldex® |
| YUPLENE® R366Y | SK Global Chemical | PP Random Copolymer | YUPLENE® |
| NYLOY® MG-8030N-V 60BK1 | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |
| Catalyst PS/2LRO | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| LNP™ LUBRICOMP™ DFL36ELH compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |