Category: | PP Homopolymer , Polypropylene Homopolymer |
Manufacturer: | Jackdaw Polymers |
Trademark: | Jackdaw PP |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | oUdtRp_Jackdaw-PP-EP16BK6600.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
Jackdaw PP EP16BK6600 is a Polypropylene Homopolymer (PP Homopolymer) product filled with 20% glass bead and 10% glass fiber. It is available in Europe. Primary characteristic: homopolymer. |
General Information | |
---|---|
Filler / Reinforcement |
|
Features |
|
Appearance |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength (Break) | 38.0 | MPa | ASTM D638, ISO 527-2 |
Tensile Elongation (Break) | 25 | % | ASTM D638, ISO 527-2 |
Flexural Modulus | 3400 | MPa | ASTM D790, ISO 178 |
Flexural Strength | 45.0 | MPa | ASTM D790, ISO 178 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact Strength | 12 | kJ/m² | ISO 180 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load | |||
0.45 MPa, Unannealed | 136 | °C | ASTM D648, ISO 75-2/B |
1.8 MPa, Unannealed | 129 | °C | ASTM D648, ISO 75-2/A |
Melting Temperature | 175 | °C | ISO 1218, ASTM D2117 |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
RTP 3099 X 99462 | RTP Company | PMP | RTP |
RTP ESD C 202 H | RTP Company | Nylon 66 | RTP |
TORZEN® G3000HR BK34 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
Wellamid® 42L-NBK1 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
NaturePlast PHE 008 | NaturePlast | PHA | NaturePlast |