DuPure® R 50
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ducor Petrochemicals BV |
| Trademark: | DuPure® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oUVAFz_DuPure-R-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description DuPure R 50 is a polypropylene homopolymer with a narrow/medium molecular weight distribution, and is formulated with a general purpose additivation package. The product shows a good flowability. Applications DuPure R 50 is suitable for: general purpose injection moulding, e.g. closures, furniture and houseware. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 78.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1550 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 8.0 | % | |
| Break | > 50 | % | |
| Tensile Creep Modulus 1(1000 hr) | 380 | MPa | ISO 899-1 |
| Shear Modulus | 800 | MPa | ISO 6721-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 1.5 | kJ/m² | |
| 23°C | 3.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 14 | kJ/m² | |
| 23°C | 110 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 1.3 | kJ/m² | |
| 23°C | 3.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 85.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 154 | °C | ISO 306/A |
| -- | 90.0 | °C | ISO 306/B |
| Melting Temperature (DSC) | 163 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (1000 µm) | 60 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | elongation <0.5% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nanjing Hongrui PA6 B500 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 6 | Nanjing Hongrui PA6 |
| GLAMIDE® T-808-02 | TOYOBO America, Inc. | Nylon 6 | GLAMIDE® |
| GTPO™ 8290 | S&E Specialty Polymers, LLC | TPO (POE) | GTPO™ |
| Hostaform® MT® SlideX™ 2404 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| LNP™ STAT-KON™ QE002S compound | SABIC Innovative Plastics | Nylon 610 | LNP™ STAT-KON™ |