SAXAMID™ 226F4RY01
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SAX Polymers |
| Trademark: | SAXAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oUHfmx_SAXAMID-226F4RY01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SAXAMID 226F4RY01 is a polyamide 6.6 injection-molding-grade reinforced with 20 % glass fibres. This grade is equipped with a halogeneous-free flame retardant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 150 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8300 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 118 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 6700 | MPa | ISO 178 |
| Flexural Stress 2 | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.5 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 46 | kJ/m² | |
| 23°C | 57 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 6.5 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 39 | kJ/m² | |
| 23°C | 45 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 60.0 mm Span) | 239 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 248 | °C | ISO 306/B120 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 750 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 280 to 295 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SynPlast™ DOA-N | PolyOne Corporation | Di (2-ethylhexyl) Adipate | SynPlast™ |
| Flontech® FT-1-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Fluoroloy® A15 | Saint Gobain Performance Plastics | TP, Unspecified | Fluoroloy® |
| KRALASTIC® KU-650 R-1 | Nippon A&L Inc. | ABS | KRALASTIC® |
| LUVOCOM® 1-7701 VP | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |