INEOS PP N05U-00
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oTdvUb_INEOS-PP-N05U-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| N05U-00 is an extrusion-grade nucleated impact copolymer polypropylene resin designed for fiber optic buffer tube applications in the protection of glass fibers. N05U-00 has an excellent impact/stiffness property balance and provides the high compression strength required to meet the Bellcore GR-20-CORE standard (Generic Requirements for Optical Fiber and Fiber Optic Cable). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.907 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 89 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 26.9 | MPa | |
| Break | 19.2 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 5.2 | % | |
| Break | 130 | % | |
| Flexural Modulus - 1% Secant | 1490 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 64 | J/m | |
| 23°C | 400 | J/m | |
| Notched Izod Impact (Area) | ASTM D256 | ||
| -20°C | 6.20 | kJ/m² | |
| 23°C | 38.7 | kJ/m² | |
| Instrumented Impact, Ductility | ASTM D3763 | ||
| -20°C | Ductile | ||
| 23°C | Ductile |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 106 | °C | |
| 1.8 MPa, Unannealed | 57.2 | °C | |
| Vicat Softening Temperature | 151 | °C | ASTM D1525 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 64 | ASTM D2457 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® CP 1502 BK | Plastic Solutions, Inc. | PP Impact Copolymer | PrimaFlex® |
| Witcom POM-C 2012/300 EXP2 | Witcom Engineering Plastics B.V. | Acetal (POM) Copolymer | Witcom POM-C |
| Evatane® 42-60 | Arkema | EVA | Evatane® |
| Generic PBT - Glass Bead\Glass Fiber | Generic | PBT | Generic |
| SIBUR Synthetic Rubber SBR-1706 Grade B | SIBUR | SBR, Emulsion | SIBUR Synthetic Rubber |