Edgetek™ AT-15GB/000 BK023
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oTaWiw_Edgetek-AT-15GB-000-BK023.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Edgetek™AT-15GB/000 BK023 is a polyoxymethylene (POM) copolymer product containing 15% glass beads. It can be processed by injection molding and is available in the Asia-Pacific region. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.5 - 1.9 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 47.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2500 | MPa | ASTM D790 |
| Flexural Strength 3 | 75.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 45 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 96.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 190 - 200 | °C | |
| Middle Temperature | 190 - 200 | °C | |
| Front Temperature | 190 - 200 | °C | |
| Mold Temperature | 75.0 - 85.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP PPC1GF2UV-RXF | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| Unilex™ UP.32.955 | United Polychem | HDPE | Unilex™ |
| NuSil CV3-2640 | NuSil Technology | Silicone | NuSil |
| Boda BDF45P | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Ateva® 2821A | Celanese EVA Performance Polymers | EVA | Ateva® |