TAROMID B 280 Z3
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oTGtv4_TAROMID-B-280-Z3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 6 elastomer modified, very high impact resistance also at low temperature, high viscosity, very good chemical resistance to oils, solvents and other chemical substances. Available: all colors, lubricated (W), and UV-stabilized (L). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 to 1.10 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 1.2 to 1.5 | % | ASTM D955 |
| Water Absorption | |||
| 23°C, 24 hr | 0.80 | % | ASTM D570, ISO 62 |
| Saturation | 6.0 | % | ASTM D570 |
| Saturation, 23°C | 6.0 | % | ISO 62 |
| Granule Humidity | < 0.15 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1800 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 55.0 | MPa | |
| Break | 50.0 | MPa | |
| Tensile Elongation (Break) | > 150 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 1600 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1 | ASTM D256, ISO 179 | ||
| -20°C | 18 | kJ/m² | |
| 23°C | 85 | kJ/m² | |
| Charpy Unnotched Impact Strength 2 | ASTM D256, ISO 179 | ||
| -20°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | ISO 180, ASTM D256 | ||
| -20°C, 3.20 mm | 600 | J/m | |
| 23°C, 3.20 mm | 800 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 60.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/B50, ASTM D1525 3 |
| Ball Pressure Test (125°C) | Pass | VDE 0470 | |
| Melting Temperature | 220 | °C | ASTM D211, ISO 121 |
| CLTE - Flow (-30 to 30°C) | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.0E+15 | ohms·cm | ASTM D257 |
| Comparative Tracking Index (Solution A) | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.970 mm | HB | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 90.0 | °C | |
| Pre-heater | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 6x4x50 mm |
| 2 . | 6x4x50 mm |
| 3 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LXR510H | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| TEKAMID™ TB120IR | Mando Advanced Materials Co., Ltd. | Nylon 6 | TEKAMID™ |
| Baoding 6126H | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU, Unspecified | Baoding |
| BLUESTAR® 1090 | Nantong Xingchen Synthetic Material Co., Ltd. | PBT | BLUESTAR® |
| DOWLEX™ 2045.01 G | The Dow Chemical Company | LLDPE | DOWLEX™ |