Laril 13 G/20-V1
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Laril |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oT9EUl_Laril-13-G-20-V1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Modified Polyphenylene Oxyde (PPOm). Glass fibres. UL94 V-1 classified, halogens and red phosphorous free. Product UL certified. High dimensional stability. Good thermal resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.50 to 0.70 | % | |
| Flow : 2.00 mm | 0.40 to 0.65 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 6900 | MPa | |
| 60°C | 6000 | MPa | |
| 90°C | 5400 | MPa | |
| 120°C | 3300 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 90°C | 50.0 | MPa | |
| Yield, 120°C | 25.0 | MPa | |
| Break, 23°C | 90.0 | MPa | |
| Break, 60°C | 70.0 | MPa | |
| Break, 90°C | 45.0 | MPa | |
| Break, 120°C | 20.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 90°C | 1.5 | % | |
| Yield, 120°C | 1.5 | % | |
| Break, 23°C | 2.0 | % | |
| Break, 60°C | 2.0 | % | |
| Break, 90°C | 2.2 | % | |
| Break, 120°C | 3.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 6.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 25 | kJ/m² | |
| 23°C | 25 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 75 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 130 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 125 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 115 | °C | |
| Vicat Softening Temperature | 130 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 3.0E-6 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-1 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 31 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Multi-Flex® TPE A4710 SUV | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| Borcoat™ EB133E-1199-LT | Borealis AG | PP Copolymer | Borcoat™ |
| Karina WHITE PVC COMPOUND 880-10/152-E-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaslube® HTN 01410 BK | Techmer Engineered Solutions | Nylon, Unspecified | Plaslube® |
| POLYblend PC/ABS 65H | Polykemi AB | PC+ABS | POLYblend |