LNP™ LUBRICOMP™ DL001 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oQvG8p_LNPLUBRICOMPDL001compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP LUBRICOMP DL001 is a compound based on Polycarbonate resin containing PTFE. Added features include: Internally Lubricated. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 57.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 5.6 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 2300 | MPa | ISO 178 |
| Flexural Stress | 91.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3 | |||
| 0.45 MPa, unannealed, 64.0mm span | 138 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 128 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 7.4E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 7.3E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 304 - 316 | °C | |
| Front Temperature | 310 - 321 | °C | |
| Processing (Melt) Temp | 299 - 316 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resilience™ HC 4895 | PolyOne Corporation | PVC, Rigid | Resilience™ |
| Tecnoflon® BR 9151 | Solvay Specialty Polymers | Fluorelastomer | Tecnoflon® |
| STABAMID® 25 RS 9 | Solvay Polyamide & Intermediates | Nylon 66 | STABAMID® |
| Topilene® HB240T | Hyosung Corporation | PP Impact Copolymer | Topilene® |
| Hostacom HBG H01 BLACK | LyondellBasell Industries | PP Homopolymer | Hostacom |