SD POLYCA™ CR3441-10G
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Sumika Styron Polycarbonate Limited |
| Trademark: | SD POLYCA™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oQm7Lp_SDPOLYCACR344110G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SD POLYCA CR series are PC/Polyester alloy grades. These products have improved chemical resistant property in addition to high impact property and heat resistant property of polycarbonate resin. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.30 - 0.50 | % | ASTM D955 |
| Transverse flow | 0.30 - 0.50 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 125 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 | MPa | ISO 527-2 |
| Tensile Strength | |||
| -- | 78.0 | MPa | ASTM D638 |
| -- | 80.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 4.0 | % | ASTM D638 |
| Fracture | 5.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3930 | MPa | ASTM D790 |
| -- | 4000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 123 | MPa | ASTM D790 |
| -- | 127 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 125 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 120 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 115 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Lateral | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POWERSIL® XLR® 620 A/B | Wacker Chemie AG | Silicone | POWERSIL® |
| Tarnamid® T-27 GF25 MT15 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| FORMULA P COMP 3240 | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |
| Generic PPS | Generic | PPS | Generic |
| Kepital® FW-21 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |