LNP™ LUBRICOMP™ XFL36 compound
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oQdzUx_LNP-LUBRICOMP-XFL36-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP XFL36 is a compound based on Amorphous Nylon containing 30% Glass Fiber and 15% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound XFL-4036 Product reorder name: XFL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr, 50% RH) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 127 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 3.0 to 4.0 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 7930 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 50.0 mm Span) | 172 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C) | 270 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 137 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 6.0 to 12 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 290 to 300 | °C | |
| Processing (Melt) Temp | 260 to 300 | °C | |
| Mold Temperature | 50.0 to 100 | °C | |
| Back Pressure | 0.170 to 0.340 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM SN601G40AH | RJM International, Inc. | Nylon 66 | RJM |
| TRILAC® ABS-MP1000 | Polymer Technology and Services, LLC | ABS | TRILAC® |
| Karina GRAY PVC COMPOUND 732D18/87-G-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OmniPro™ HPP CCF40 | OMNI Plastics, LLC | PP Homopolymer | OmniPro™ |
| Sylvin 9077-95LMW Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |