LNP™ STAT-KON™ RE002 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oQDSuB_LNP-STAT-KON-RE002-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON RE002 is a compound based on Nylon 66 resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound RC-1002 Product reorder name: RE002 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.60 to 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 1.0 to 3.0 | % | ASTM D955 |
| Across Flow : 24 hr | 1.3 | % | ISO 294-4 |
| Flow : 24 hr | 0.74 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.80 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8270 | MPa | ASTM D638 |
| -- | 7800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 134 | MPa | ASTM D638 |
| Yield | 131 | MPa | ISO 527-2 |
| Break | 127 | MPa | ASTM D638 |
| Break | 131 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.3 | % | ASTM D638 |
| Yield | 2.1 | % | ISO 527-2 |
| Break | 2.3 | % | ASTM D638 |
| Break | 2.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 6890 | MPa | ASTM D790 |
| -- | 6000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 207 | MPa | ASTM D790 |
| -- | 191 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 27 | J/m | ASTM D256 |
| 23°C 2 | 3.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 360 | J/m | ASTM D4812 |
| 23°C 3 | 24 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 5.90 | J | ASTM D3763 |
| -- | 1.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 259 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 254 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 245 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 241 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.3E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 2.9E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 to 1.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 281.3D | RTP Company | Nylon 612 | RTP |
| Axiall PVC 28930 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Ecoflex® Supersoft 00-50 | Smooth-On, Inc | Silicone | Ecoflex® Supersoft |
| ELASTOSIL® P 7684/40 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® P |
| NORYL™ SA90 resin | SABIC Innovative Plastics | PPE | NORYL™ |