POLYTROPE® STR 1030EU-01 NATURAL
| Category: | Polyolefin, Enhanced TPO , Enhanced TPO Polyolefin |
| Manufacturer: | A. Schulman Inc. |
| Trademark: | POLYTROPE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oPtUU2_POLYTROPE-STR-1030EU-01-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYTROPE STR 1030EU resin is a high melt strength thermoformable TPO that provides high impact resistance & high stiffness, enabling processors and end users to reduce product weight and improve processing efficiency without sacrificing product performance. It can be extruded in smooth or textured surfaces, or co-extruded with a POLYTROPE STR enhanced polyolefin cap resin to further customize its' durability, appearance, or feel for interior and exterior applications. The capability of POLYTROPE STR 1030EU to provide an exceptionally smooth surface in extrusion and thermoforming makes it well suited to lamination processes with decorative films. It is also easily colored and is paintable by standard TPO paint systems. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.08 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.45 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C, 24 hr, 3.18 mm) | 0.70 to 0.90 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 2(Yield, 23°C) | 23.2 | MPa | ISO 527-2 |
| Tensile Strain 3(Break, 233°C) | 360 | % | ISO 527-2 |
| Flexural Modulus - Chord 4(23°C) | 2240 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact - Flow | ASTM D256 | ||
| -30°C, 3.18 mm, Injection Molded | 180 | J/m | |
| 23°C, 3.18 mm, Injection Molded | No Break | ||
| Instrumented Dart Impact (-30°C, Total Energy, Ductile Failure) | 40.1 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 106 | °C | ISO 75-2/Bf |
| CLTE - Flow (-30 to 100°C) | 4.1E-5 | cm/cm/°C | ASTM E831 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm, All Colors) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°, 3180 µm, Thermoformed, Smooth) | 20 to 40 | ISO 2813 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Sag - 8 inch span, two point support (149°C, 3.20 mm) | 0.00 | mm | ASTM D3769 |
| Note Message | |
|---|---|
| 1 . | Method A |
| 2 . | Type 1, 50 mm/min |
| 3 . | Type 1, 50 mm/min |
| 4 . | Type 1A, 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sypex S1420GN | Ginar Technology Co., LTD. | SAN | Sypex |
| Cheng Yu A778 | Cheng Yu Plastic Company Limited | ABS | Cheng Yu |
| EpoxAcast® 690 | Smooth-On, Inc | Epoxy | EpoxAcast® |
| LNP™ LUBRILOY™ D20001 compound | SABIC Innovative Plastics | PC | LNP™ LUBRILOY™ |
| Plaslube® PPA AL20 HS L | Techmer Engineered Solutions | PPA | Plaslube® |