OmniLon™ PA6/6 U GMR40 BK1000
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniLon™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oPpGEk_OmniLon-PA6-6-U-GMR40-BK1000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% Glass/Mineral Reinforced, Nylon 6/6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 102 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 7930 | MPa | ASTM D790 |
| Flexural Strength | 172 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 254 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 271 to 293 | °C | |
| Middle Temperature | 271 to 293 | °C | |
| Front Temperature | 271 to 304 | °C | |
| Nozzle Temperature | 271 to 293 | °C | |
| Processing (Melt) Temp | 271 to 293 | °C | |
| Mold Temperature | 26.7 to 82.2 | °C | |
| Back Pressure | 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAMAT 5003S3 | POLYROCKS CHEMICAL CO., LTD | PP, Unspecified | SAMAT |
| Sylvin 9708-80C Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Franprene TGA 2345LMO | Franplast S.r.l. | TPE | Franprene |
| LNP™ LUBRICOMP™ YL003C compound | SABIC Innovative Plastics | TPEE | LNP™ LUBRICOMP™ |
| LNP™ VERTON™ MV00AS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ VERTON™ |