LNP™ LUBRICOMP™ KAL22 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oPOUWI_LNP-LUBRICOMP-KAL22-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP KAL22 is a compound based on Acetal Copolymer resin containing PTFE, Aramid Fiber. Also known as: LNP* LUBRICOMP* Compound KAL-4022 Product reorder name: KAL22 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 1.8 to 2.2 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 56.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 11 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 2900 | MPa | ISO 178 |
| Flexural Stress | 61.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.23 | ||
| vs. Itself - Static | 0.16 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 0.00 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 8.00 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed, 64.0 mm Span) | 87.0 | °C | ISO 75-2/Af |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ratron® 250C6-WR | Asia International Enterprise (Hong Kong) Limited | PESU | Ratron® |
| TECHNYL® A 218 V35 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| APEX® 3800-75NT1 | Teknor Apex Company | PVC, Flexible | APEX® |
| Comco PA 66 extruded | Comco-Plastic GmbH | Nylon 66 | Comco |
| Karina IVORY PVC COMPOUND 750-35/ 1-J-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |