SEALUTION™ 230 Peel Polymer
| Category: | POP , Peel Polymer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | SEALUTION™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oOdBdP_SEALUTION-230-Peel-Polymer.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SEALUTION™ 230 Peel Polymer is a high clarity peelable sealant that gives a peelable seal to itself, polypropylene and polyethylene. It is suitable for use in cast film lines. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.897 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.3 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Seal Initiation Temperature 1(51 µm, Blown Film) | 95.0 | °C | Internal method |
| Peelable range 2 | 95 - 180 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze 3(50.0 µm, Blown Film) | < 10 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 230 | °C |
| Extrusion instructions |
|---|
| Fabrication Conditions For Cast Film: Die Gap: 1.5 mm Melt Temperature: 190-230°C Coextruded cast film: Total film thickness: 50 microns A / B Coex, 80% / 20% layer ratio A = LLDPE/LDPE blend or random PP (40 µm) B = SEALUTION 230 (10 µm) |
| Note Message | |
|---|---|
| 1 . | Temperatures at which 2 N/15 mm heat seal strength is achieved.Heat Seal Strengths, Topwave HT Tester 0.5 s dwell, 500 N pressure, pull speed 100 mm/min. |
| 2 . | Peelable range of 3-5 N/15 mm. for this particular structure, seal to itself.Heat Seal Strengths, Topwave HT Tester 0.5 s dwell time, 500 N pressure, pull speed 100 mm/min. |
| 3 . | Haze for this particular structure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pomalux® Medical | Westlake Plastics Company | Acetal (POM) Copolymer | Pomalux® |
| Aegis® H135MP | Honeywell | Nylon 6 | Aegis® |
| FHR Polypropylene P5L2Z-038 | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| FERREX® GPP20CC56HB BLUE | Ferro Corporation | PP Homopolymer | FERREX® |
| TAFMER™ H-5030S | Mitsui Chemicals, Inc. | PAO | TAFMER™ |