LNP™ THERMOCOMP™ DX10311X compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oODtWX_LNP-THERMOCOMP-DX10311X-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DX10311X is 30% glass fiber reinforced, impact modified polycarbonate resin. High flow and good ductility. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (300°C/2.16 kg) | 9.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.10 to 0.40 | % | |
| Across Flow : 3.20 mm | 0.20 to 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8690 | MPa | ASTM D638 |
| -- | 8610 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 114 | MPa | ASTM D638 |
| Break | 115 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.5 | % | ASTM D638 |
| Break | 2.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- | 7410 | MPa | ASTM D790 |
| -- 4 | 7450 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 180 | MPa | ASTM D790 |
| -- | 180 | MPa | ISO 178 |
| -- | 172 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 17 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/2U |
| Notched Izod Impact (23°C) | 170 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 720 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) | 125 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 2.1E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.8E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 250 to 280 | °C | |
| Middle Temperature | 280 to 320 | °C | |
| Front Temperature | 280 to 320 | °C | |
| Nozzle Temperature | 280 to 320 | °C | |
| Processing (Melt) Temp | 280 to 320 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 30 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LTR662 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| TEREZ PA 6.6 HT 7500 GF 60 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Derakane® 8084 | Ashland Performance Materials | Vinyl Ester | Derakane® |
| LNP™ THERMOCOMP™ UC008H compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |
| LNP™ STAT-LOY™ A3000T compound | SABIC Innovative Plastics | ABS | LNP™ STAT-LOY™ |