Generic OBC
| Category: | OBC , Olefin Block Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oNcv84_Generic-OBC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic OBC This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.866 to 0.877 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 to 15 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 55 to 83 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1.30 to 3.82 | MPa | ASTM D638 |
| Tensile Strength (Break, 23°C) | 1.21 to 13.2 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 370 to 1500 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 3.00 to 17.0 | MPa | ASTM D412 |
| Tensile Elongation (Break, 23°C) | 770 to 2200 | % | ASTM D412 |
| Tear Strength (23°C) | 17.0 to 52.0 | kN/m | ASTM D624 |
| Compression Set | 15 to 46 | % | ASTM D395 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 119 to 120 | °C | ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radiflam® A FR 308 NER | Radici Plastics | Nylon 66 | Radiflam® |
| ACCUTECH™ CP0436M30CL | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Iupilon® FPR3500 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| Plexiglas® V825-HID | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |
| Wanthane® WHT-1172IC | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |