Tribocomp® PA66 LGF30 PTFE18 N6
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Tribocomp® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oNGPag_TribocompPA66LGF30PTFE18N6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Tribocomp® PA66 LGF30 TS0 S8, is a 30% long glass fiber reinforced black high-flow PA 66 with a pellet length of 8mm and contains 15% PTFE having excellent tribological performance. It can easily be processed on most injection molding machines. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ISO 1183 |
| shrinkage- Flow | 0.40 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.4 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 10500 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 195 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 8300 | MPa | ISO 178 |
| Flexural Stress (23°C) | 260 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 | ||
| Dynamic | 0.23 | ASTM D3702 | |
| Static | 0.18 | ASTM D3702 | |
| Wear Factor | 13.0 | ASTM D3702 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion | 2.9E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms/sq | ASTM D257 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 19 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 65 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 255 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 253 | °C | ISO 75-2/A |
| Thermal Conductivity | 0.29 | W/m/K | ISO 22007 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (2.00 mm) | 35 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 270 - 300 | °C | |
| Middle Temperature | 270 - 300 | °C | |
| Front Temperature | 285 - 300 | °C | |
| Nozzle Temperature | 285 - 310 | °C | |
| Processing (Melt) Temp | < 300 | °C | |
| Mold Temperature | 80 - 140 | °C |
| Injection instructions |
|---|
| Pre-drying -- Since polyamides are hygroscopic materials as well as sensitive to moisture during processing, this product should always be pre-dried.Regrind -- Regrind of highly filled thermoplastic materials, such as this material, should only be recycled with special care. The regrind content must never exceed 15%, and only regrind of optimum quality should be used. In any case, part properties should be checked. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wanthane® WHT-1598 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| Braskem PE SGF4950 | Braskem | HDPE | Braskem PE |
| K-vinyl 105 Deg C Rating Insulation (90-Wet) | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| TECACOMP® PA66 TC grey 3973 | Ensinger GmbH | Nylon 66 | TECACOMP® |
| SABIC® HDPE M864EG | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |