Styrolution PS 168N/L
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Styrolution PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oMoxts_Styrolution-PS-168N-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Styrolution PS 168N/L is a high molecular weight, heat resistant grade with high mechanical strength. It is suitable for physically or chemically expanded extruded sheet. It is also suitable for use as blend component with high impact polystyrene or Styrolux. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (200°C/5.0 kg) | 1.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.30 to 0.60 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | < 0.10 | % | |
| Equilibrium, 23°C, 50% RH | < 0.10 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 150 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3300 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 59.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 3300 | MPa | |
| 1000 hr | 2600 | MPa | |
| Flexural Stress | 106 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | < 25 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 98.0 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 86.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 108 | °C | ISO 306/A120 |
| -- | 101 | °C | ISO 306/B120 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.17 | W/m/K | DIN 52612 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+18 | ohms·cm | IEC 60093 |
| Dielectric Constant (100 Hz) | 2.50 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 9.0E-5 | ||
| 1 MHz | 5.0E-5 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 1 | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 180 to 280 | °C | |
| Mold Temperature | 40.0 | °C | |
| Injection Velocity | 200 | mm/sec |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 250 | °C |
| Note Message | |
|---|---|
| 1 . | Antwerp Only |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8463-60 Black | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |
| Desmopan® DP 6590A MVT | Covestro - PUR | TPU, Unspecified | Desmopan® |
| Duron PA 6,6 33GF-IML | ProPolymers Inc. | Nylon 66 | Duron |
| Braskem PE LDF0823 | Braskem IDESA | LDPE | Braskem PE |
| FUDOWPREMIX® FP55 | Fudow Co., Ltd. | Polyester, TS | FUDOWPREMIX® |