Order Products : sales@su-jiao.com
Chemlon® 235G
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oMS6CW_Chemlon-235G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 235G is a 35% glass fibre reinforced nylon 6 that offers a balance between mechanical performance, surface finish and mould release characteristics. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.41 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | 0.70 - 1.2 | -- | % | Internal method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.9 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | 8000 | MPa | ISO 527-2 |
| Tensile Stress | 180 | 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | 6.0 | % | ISO 527-2 |
| Flexural Modulus | 9200 | 4500 | MPa | ISO 178 |
| Flexural Stress | 260 | 140 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 17 | 37 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 55 | -- | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | 14 | -- | kJ/m² | ISO 180/A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | > 200 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | > 200 | -- | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.00 mm) | 11 | 8.0 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.80 | 4.20 | IEC 60250 | |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.50 mm, Teknor Apex test result) | HB | -- | UL 94 | |
| Oxygen Index | 24 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 20 | hr | |
| Rear Temperature | 250 - 280 | °C | |
| Middle Temperature | 250 - 280 | °C | |
| Front Temperature | 250 - 280 | °C | |
| Processing (Melt) Temp | 250 - 290 | °C | |
| Mold Temperature | 70.0 - 90.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | Low | ||
| Screw Speed | Moderate |
| Injection instructions |
|---|
| No drying is necessary unless the material has been exposed to air for longer than three hours. The appearance of splash marks on the surface of mouldings indicates excessive moisture is present. |
| Note Message | |
|---|---|
| 1 . | Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding). |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1405 HF TFE 5 | RTP Company | PESU | RTP |
| Shin-Etsu Elastomer KE-5006U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Unipren® Elastomers A3 NTLA010 65A UP323 | Petropol Industry and Trade of Polymers LTDA | SEBS | Unipren® Elastomers |
| Celstran® PA66-GF30-07 | Celanese Corporation | Nylon 66 | Celstran® |
| 3M™ Dyneon™ Fluoroelastomer FPO 3630 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |