Durethan® BKV 60 H2.0 EF DUS060 900116
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oLY896_DurethanBKV60H20EFDUS060900116.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 60 % glass fibers, injection molding, improved flowability, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.70 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.75 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 280°C, 2.00mm 1 | 0.40 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.060 | -- | % | ISO 2577 |
| Flow direction : 280°C, 2.00mm 3 | 0.32 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.030 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 3.6 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.3 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 255 | 155 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 20000 | 12000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 225 | 145 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.4 | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 19300 | 12800 | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 365 | 235 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 2.8 | 3.6 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GHR, 10-220, GF60 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.060 - 0.20 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 16 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 16 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 90 | 90 | kJ/m² | ISO 179/1eU |
| 23°C | 90 | 90 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 16 | -- | kJ/m² | ISO 180/1A |
| 23°C | 16 | 20 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 80 | 80 | kJ/m² | ISO 180/1U |
| 23°C | 80 | 80 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 213 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 210 | -- | °C | ISO 306/B120 |
| Melting Temperature 8 | 222 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 1.2E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 7.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity (23°C) | 5.8E+14 | 8.0E+11 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C, 1.00 mm) | 33 | 33 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 23°C, 100 Hz | 5.30 | 11.2 | IEC 60250 | |
| 23°C, 1 MHz | 4.70 | 5.10 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 23°C, 100 Hz | 0.016 | 0.21 | IEC 60250 | |
| 23°C, 1 MHz | 0.018 | 0.065 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds PP-6462 | Ravago Manufacturing Americas, LLC | PP Homopolymer | Ravago Compounds |
| Baytec® ME-230 (74A) | Covestro - PUR | PUR-Ether/MDI | Baytec® |
| BCC Resins MB1200 | BCC Products Inc. | PUR, Unspecified | BCC Resins |
| Crastin® HR5330HF BK503 | DuPont Performance Polymers | PBT | Crastin® |
| DJSilicone NE-Z260 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |