NEFTEKHIM PP PP6129K
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Nizhnekamskneftekhim Inc. |
| Trademark: | NEFTEKHIM PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oLCLdo_NEFTEKHIM-PP-PP6129K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product obtained by polymerization of propylene in presence of complex organic metal catalysts. Polypropylene homopolymer possesses increased long-term thermal stability, stability to thermo-oxidative destruction in the process of PP production, PP processing and PP articles usage. Improved properties, preventing sticking of film layers. Application: biaxial oriented multilayer metallized film. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 650 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 118 | °C | ASTM D1525 |
| Additional Information |
|---|
| Melt Mass-Flow Rate (MFR), ASTM D1238, 230°C/2.16kg: 4.0 to 6.0 g/10min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3896 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| QR Resin QR-1025-FR | QTR, Inc. | PC | QR Resin |
| Vi-Chem PVC V221-77 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Nymax™ 1010 A Natural | PolyOne Corporation | Nylon 6 | Nymax™ |
| King Pearl® G-L | Loyal Chemical | PS (EPS) | King Pearl® |