ALCUDIA® LDPE 2203FA
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oL7hzG_ALCUDIA-LDPE-2203FA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCUDIA® 2203FA is a low density polyethylene grade, produced by high pressure autoclave technology, suitable for blown or cast film applications. This material offers easy processability and good balance of mechanical properties. It contains antiblock additives. TYPICAL APPLICATIONS
Recommended melt temperature range from 170 to 220°C. Processing conditions should be optimised for each production line. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.922 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.40 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 25.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 23.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 400 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 600 | % | ISO 527-3 |
| Dart Drop Impact (40 µm, Blown Film) | 450 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 40 µm, blown film | 4.0 | N | ISO 6383-2 |
| TD : 40 µm, blown film | 6.0 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ISO 306/A |
| Additional Information |
|---|
| Data taken from 40 µm thickness film, blow up ratio 2.5:1. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BP Flex A 6310 BLK | Buckeye Polymers, Inc. | TPE | BP Flex |
| Karina IVORY PVC COMPOUND 90850-35/ 1-AY-ACE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ MFL36S compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ LUBRICOMP™ |
| Plaslube® POM HO TL10 | Techmer Engineered Solutions | Acetal (POM) Homopolymer | Plaslube® |
| POLYCASA® ACRYL KR 2007/1 | Polycasa | Acrylic (PMMA) | POLYCASA® ACRYL |