Vydyne® R530HT BK02
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ascend Performance Materials Operations LLC |
| Trademark: | Vydyne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oKMB9h_Vydyne-R530HT-BK02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vydyne R530HT BK02 product description to come Typical Applications/End Uses: To come |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 23°C, 2.00 mm | 0.90 | -- | % | |
| Flow : 23°C, 2.00 mm | 0.40 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.90 | -- | % | |
| Equilibrium, 50% RH | 1.9 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9800 | 6900 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 185 | 125 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.5 | 4.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 8800 | 5500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 260 | 170 | MPa | ISO 178 |
| Poisson's Ratio (23°C) | 0.40 | -- | ISO 527 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 7.0 | 8.0 | kJ/m² | |
| 23°C | 15 | 16 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 65 | 70 | kJ/m² | |
| 23°C | 70 | 100 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | |||
| -30°C | 11 | 11 | kJ/m² | |
| 23°C | 11 | 11 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 258 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 248 | -- | °C | ISO 75-2/A |
| Melting Temperature | 258 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C, 2.00 mm | 2.2E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C, 2.00 mm | 1.1E-4 | -- | cm/cm/°C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 280 to 310 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 280 to 310 | °C | |
| Nozzle Temperature | 280 to 310 | °C | |
| Processing (Melt) Temp | 285 to 305 | °C | |
| Mold Temperature | 65.0 to 95.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ATTANE™ SL 4102G | The Dow Chemical Company | ULDPE | ATTANE™ |
| KumhoSunny PC HCG2520 | Shanghai KumhoSunny Plastics Co., Ltd. | PC | KumhoSunny PC |
| Lifoflex® GA 1040 | Müller Kunststoffe GmbH | SEBS | Lifoflex® |
| Formolene® 2613N | Formosa Plastics Corporation, U.S.A. | PP Copolymer | Formolene® |
| Panlite® ML-5206ZLP | TEIJIN LIMITED | PC | Panlite® |