DOW™ LDPE 410F

Category:	LDPE , Low Density Polyethylene Resin
Manufacturer:	The Dow Chemical Company
Trademark:	DOW™ LDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	oISg3F_DOW-LDPE-410F.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

DOW LDPE 410F Low Density Polyethylene Resin is a high clarity resin designed for lamination film and clarity over wrap applications. This resin does not contain slip and antiblock additives. It can be readily extruded using conventional blown film techniques utilizing melt temperatures between 170 and 195°C; and cast film using temperatures between 180 and 220°C. This resin when properly fabricated shows: excellent processability and draw down, outstanding toughness and impact properties, superior optical properties, excellent tensile and tear strength.

Main Characteristics:

DOW LDPE 410F Low Density Polyethylene Resin should comply with FDA regulation 177.1520 and with most European food contact regulations when used unmodified and processed according to good manufacturing practices for food contact applications. Please, contact your nearest Dow office for food contact compliance statements. The purchaser remains responsible for determining whether the use complies with all relevant regulations.

Slip Additive: none
Antiblock Additive: none

General Information
Agency Ratings	FDA 21 CFR 177.1520
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.925	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	2.0	g/10 min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Coefficient of Friction (vs. Itself - Dynamic)	0.60 - 0.80		ASTM D1894

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	50	µm
secant modulus			ASTM D882
2% secant, MD : 50 µm	190	MPa	ASTM D882
2% secant, TD : 50 µm	200	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Yield, 50 µm	10.0	MPa	ASTM D882
TD : Yield, 50 µm	11.0	MPa	ASTM D882
MD : Break, 50 µm	22.0	MPa	ASTM D882
TD : Break, 50 µm	20.0	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Break, 50 µm	450	%	ASTM D882
TD : Break, 50 µm	650	%	ASTM D882
Dart Drop Impact (50 µm)	110	g	ASTM D1709A
Elmendorf Tear Strength			ASTM D1922
MD : 50 µm	500	g	ASTM D1922
TD : 50 µm	400	g	ASTM D1922

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	96.0	°C	ISO 306/A

Optical	Nominal Value	Unit	Test Method
Gloss (20°, 50.0 µm)	80		ASTM D2457
Haze (50.0 µm)	6.9	%	ASTM D1003

Extrusion	Nominal Value	Unit
Melt Temperature	170 - 195	°C

Extrusion instructions
吹塑薄膜的制造条件：放大比 2.5 比 1

Resin Grade	Manufacturer	Category	Trademark
NYLOY® UB-0010N-V G30N4N	Nytex Composites Co., Ltd.	Nylon, Unspecified	NYLOY®
Fainplast PVC FKA 89	Fainplast Compounds S.r.l	PVC, Unspecified	Fainplast PVC
Escorene™ Ultra LD 705.MJ Molding	ExxonMobil Chemical	EVA	Escorene™ Ultra
Karina NATURAL PVC COMPOUND 800-25/1-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
LONGLITE® PMC T308J	CCP Group	Phenolic	LONGLITE® PMC