EMERGE™ PC/ABS 7590ECO
| Category: | PC+ABS , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oIKt4L_EMERGE-PC-ABS-7590ECO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE 7590ECO Advanced Resin is an ignition-resistance PC/ABS alloy containing 35% post consumer recycled (PCR) materials and no chlorine or bromine additives. This resin provides superior processability for molding thin-wall parts and optimizing cycle time productivity in injection molding operations. Applications:
|
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 2420 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 55.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 46.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 4.0 | % | |
| Break, 3.20 mm, Injection Molded | 100 | % | |
| Flexural Modulus (3.20 mm, Injection Molded) | 2830 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Injection Molded) | 97.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 720 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.20 mm, Injection Molded) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 82.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | Internal Method | |
| Oxygen Index | 29 | % | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMSTER PF321G4 | Polyram Ram-On Industries | PBT | RAMSTER |
| Shuang-Bang CM-8205N | Shuang-Bang Industrial Corp. | Film, TPU | Shuang-Bang |
| Witcom PA66 3A/2L1 | Witcom Engineering Plastics B.V. | Nylon 66 | Witcom PA66 |
| Hifax HSBM CB 1151 G | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Polifor® E 20 TX/30 AS UV NATURALE | SO.F.TER. SPA | PP Copolymer | Polifor® |