Moplen COAT EP/60 BIANCO
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oIItCZ_Moplen-COAT-EP-60-BIANCO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
"Moplen" COAT EP/60 BIANCO is a UV and thermal stabilized polypropylene copolymer, designed for extrusion. It is developed for continuous service at high temperature (to be designed case by case, but typically in the -20°C/+120°C temperature range for on-shore projects and up to +145°C for offshore projects). This product offers good resistance to impact, indentation, environmental stress cracking, chemicals, fungi and bacteria, as well as good stiffness and low water absorption. This grade is available in white, in pellet form. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.80 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (F0) | > 2000 | hr | ASTM D1693 |
| Water Content | < 0.050 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (220°C) | > 40 | min | ASTM D3895 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | > 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 22.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 400 | % | ISO 527-2 |
| Flexural Modulus | 1000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 5.0 | kJ/m² | |
| 23°C | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 145 | °C | ISO 306/A50 |
| Melting Temperature | 240 to 250 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 240 to 260 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA A3 BRC0001 NR349 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| LNP™ LUBRICOMP™ GFL36L compound | SABIC Innovative Plastics | PSU | LNP™ LUBRICOMP™ |
| PERCOM® KHT20 GW800 | A. Schulman Europe | PP, Unspecified | PERCOM® |
| Hostacom TRC 2016N | LyondellBasell Industries | PP Copolymer | Hostacom |
| Sylvin 8999-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |