XIRAN® SG230 are SMA (styrene maleic anhydride) based injection molding compounds with:
XIRAN® SG230 is available in a standard black (B), natural (N) and an extra deep black version (EB-B) Application areas XIRAN® SG230 is a 15% glass filled injection molding compound designed for applications with high stiffness-strength. These products are very suitable for painted and foamed parts, high temperature resistance and precision parts with high shot to shot consistency. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 3.0 | g/10 min | ISO 1133 |
| Spiral Flow 1 | 35.0 | cm | Internal Method |
| Molding Shrinkage 2 | Internal Method | ||
| Across Flow | 0.61 | % | |
| Flow | 0.25 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Flexural Modulus | 5400 | MPa | ISO 178 |
| Flexural Stress | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 8.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -40°C | 32 | kJ/m² | |
| 23°C | 28 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -40°C | 8.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 125 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 120 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 122 | °C | ISO 306/B |
| CLTE | ASTM D696 | ||
| Flow : -30 to 80°C | 4.2E-5 | cm/cm/°C | |
| Transverse : -30 to 80°C | 5.5E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Nozzle Temperature | 245 to 275 | °C | |
| Processing (Melt) Temp | < 285 | °C |
| Note Message | |
|---|---|
| 1 . | 2 mm |
| 2 . | Measured according to the Autodesk Mold flow Plastics Labs using a tag mold. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wah Hong UP WH-8100-BLK D | Wah Hong Industrial Corp. | Polyester Alloy | Wah Hong UP |
| EPO-TEK® P1011 | Epoxy Technology Inc. | PI, TS | EPO-TEK® |
| HiFill® PSU GF20 BK | Techmer Engineered Solutions | PSU | HiFill® |
| InnoPlus LD2026K | PTT Global Chemical Public Company Limited | LDPE | InnoPlus |
| Polimid B AV | Poliblend S.p.a. | Nylon 6 | Polimid B |