Karina IVORY PVC COMPOUND 809D35/ 1-C-IS-LMP
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oG7U4n_Karina-IVORY-PVC-COMPOUND-809D35-1-C-IS-LMP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HEAVY METAL FREE PVC COMPOUND RECOMMENDED FOR EXTRUSION OF COAXIAL CABLES JACKET AND IN ACCORDANCE TO THE ROHS. |
| General Information | |
|---|---|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.33 to 1.39 | g/cm³ | IEC 60811-1-3 |
| Cadmium Content | < 50 | ppm | ASTM D1971 |
| Chromium Content | < 100 | ppm | ASTM D1971 |
| Color | OK | ME 12 | |
| Color a | -1.96 to 1.04 | ME 12 | |
| Color b | 4.18 to 7.18 | ME 12 | |
| Color L | 86.9 to 89.9 | ME 12 | |
| Mercury Content | < 100 | ppm | ASTM D1971 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bromine Content | < 100 | ppm | IEC 62321 |
| Lead Content | < 100 | ppm | ASTM D1971 |
| Maximum Variation of Elongation | < 25 | % | IEC 60811-1-2 |
| Maximum Variation of Tensile Strength | < 25 | % | IEC 60811-1-2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 78 to 82 | NBR 7456 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | > 12.6 | MPa | IEC 60811-1-1 |
| Tensile Strain (Yield) | > 130 | % | IEC 60811-1-1 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 12.6 | MPa | IEC 60811-1-2 |
| Tensile Elongation 3(Break) | > 130 | % | IEC 60811-1-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 1.0E+13 | ohms·cm | NBR 5403 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | > 28 | % | NBR 6245 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 100°C |
| 3 . | Aged in Air for 168 hr at 100°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nycal™ 2150MC40 | Technical Polymers, LLC | Nylon 66 | Nycal™ |
| Durez® 33668 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| INSTRUC PCPETGF30 | Infinity LTL Engineered Compounds | PC+PET | INSTRUC |
| Leona™ 14G25 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| LEXAN™ 131 resin | SABIC Innovative Plastics | PC | LEXAN™ |