Petra® 330 FR BK-112
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | BASF Corporation |
| Trademark: | Petra® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oG5BTK_Petra-330-FR-BK-112.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Petra 330 FR BK-112 is a 30% glass reinforced, flame retardant PET, pigmented black injection molding compound rated UL94 V-0 in a 1/64 inch thickness. The product is designed for injection molding of thin and complex parts such as electrical bobbins. Due to its high crystallization rate the processability of the product in the injection molding process is very good. It exhibits excellent balance of properties including strength, stiffness, HDT, dimensional resistance and electrical properties. Applications Electrical/electronic application including connectors, bobbins, sockets, ciol, switches, relays, covers and housings. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.67 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Break, -40°C | 170 | MPa | |
| Break, 23°C | 135 | MPa | |
| Break, 80°C | 82.0 | MPa | |
| Break, 121°C | 60.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Break, -40°C | 2.0 | % | |
| Break, 23°C | 2.0 | % | |
| Break, 80°C | 4.1 | % | |
| Break, 121°C | 5.7 | % | |
| Flexural Modulus (23°C) | 9930 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 215 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 90 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 223 | °C | ASTM D648 |
| Peak Melting Temperature | 250 | °C | ASTM D3418 |
| RTI Elec | UL 746 | ||
| 0.300 mm | 75.0 | °C | |
| 0.750 mm | 155 | °C | |
| 1.50 mm | 155 | °C | |
| 3.00 mm | 155 | °C | |
| RTI Imp | UL 746 | ||
| 0.300 mm | 75.0 | °C | |
| 0.750 mm | 155 | °C | |
| 1.50 mm | 155 | °C | |
| 3.00 mm | 155 | °C | |
| RTI Str | UL 746 | ||
| 0.300 mm | 75.0 | °C | |
| 0.750 mm | 155 | °C | |
| 1.50 mm | 155 | °C | |
| 3.00 mm | 155 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (1.50 mm) | > 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength 1(1.50 mm) | 29 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.300 mm | V-0 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 100 to 110 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® P50N07 | Polyram Ram-On Industries | PP, Unspecified | Polytron® |
| Ultramid® B3M6 BK60564 | BASF Corporation | Nylon 6 | Ultramid® |
| KRATON® G7820 GU-N | Kraton Polymers LLC | SEBS | KRATON® |
| LNP™ LUBRICOMP™ NXCY620 compound | SABIC Innovative Plastics | PC+ABS | LNP™ LUBRICOMP™ |
| Lupolen 3026 F | LyondellBasell Industries | LDPE | Lupolen |