Borealis PE FG5190
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oFWzd4_Borealis-PE-FG5190.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FG5190 is a Butene Linear Low Density Polyethylene for Film Extrusion. Includes Antioxidant. The grade is developed for medium and heavy duty bags, bags and bin liners, dual stretch films, and film applications demanding high puncture resistance and strength. In mixtures with LD, the grade contribute to improve the draw down, seal strength and avoids bum through problems in shrinkfilm. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.2 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic) | 0.80 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Secant Modulus | ASTM D882A | ||
| MD : 40 µm | 170 | MPa | |
| TD : 40 µm | 210 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm | 12.0 | MPa | |
| TD : Yield, 40 µm | 12.0 | MPa | |
| MD : 40 µm | 39.0 | MPa | |
| TD : 40 µm | 34.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 40 µm | 740 | % | |
| TD : Break, 40 µm | 850 | % | |
| Dart Drop Impact (40 µm) | 140 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 40 µm | 1.0 | N | |
| TD : 40 µm | 6.5 | N |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 40.0 µm) | 95 | ASTM D2457 | |
| Haze (40.0 µm) | 12 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 235 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sicoklar E81.22 | Ravago Group | PC | Sicoklar |
| Duratuf™ 909U2/X | Technical Polymers, LLC | Acetal (POM) Homopolymer | Duratuf™ |
| Grilon® BG-35 S | EMS-GRIVORY | Nylon 6 | Grilon® |
| Kingfa MAC-851 | Kingfa | PC+ABS | Kingfa |
| SIBUR Synthetic Rubber NBR 2665 | SIBUR | NBR | SIBUR Synthetic Rubber |