Generic UHMWPE
| Category: | UHMWPE , Ultra High Molecular Weight Polyethylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oFKvc0_Generic-UHMWPE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic UHMWPE This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.922 to 0.949 | g/cm³ | ASTM D792 |
| 23°C | 0.930 to 0.950 | g/cm³ | ISO 1183 |
| -- | 0.924 to 0.954 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.45 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 0.0 to 0.25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 2.2 to 8.1 | % | ASTM D955 |
| Water Absorption | |||
| 23°C, 24 hr | 0.010 to 0.070 | % | ASTM D570 |
| Saturation, 23°C | 0.010 to 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| 23°C | 59 to 66 | ASTM D2240 | |
| 23°C | 57 to 64 | ISO 868 | |
| Ball Indentation Hardness | 35.0 to 38.3 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 669 to 803 | MPa | ASTM D638 |
| 23°C | 676 to 795 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 16.7 to 23.5 | MPa | ASTM D638 |
| Yield, 23°C | 17.0 to 17.6 | MPa | ISO 527-2 |
| Break, 23°C | 29.6 to 53.5 | MPa | ASTM D638 |
| Break, 23°C | 30.0 to 30.2 | MPa | ISO 527-2 |
| Ultimate, 23°C | 32.8 to 40.0 | MPa | ASTM D638 |
| Tensile Strain | |||
| Yield, 23°C | 15 to 20 | % | ISO 527-2 |
| Break, 23°C | 59 to 470 | % | ASTM D638 |
| Break, 23°C | 350 to 400 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 50 to 56 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 441 to 915 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 20.6 to 26.3 | MPa | ASTM D790 |
| Compressive Modulus | 551 to 689 | MPa | ASTM D695 |
| Compressive Strength | |||
| 23°C | 20.0 to 22.9 | MPa | ASTM D695 |
| 23°C | 4.00 to 32.0 | MPa | ISO 604 |
| Coefficient of Friction | 0.060 to 0.16 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 78 to 180 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 78.9 to 93.5 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 45.9 to 79.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 42.0 to 42.1 | °C | ISO 75-2/A |
| Continuous Use Temperature | 80.0 to 120 | °C | ASTM D794 |
| Vicat Softening Temperature | 80.0 to 128 | °C | ASTM D1525, ISO 306 |
| Peak Melting Temperature | 133 to 136 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 127 to 135 | °C | ASTM D3418 |
| CLTE - Flow | |||
| -- | 9.0E-5 to 9.2E-4 | cm/cm/°C | ASTM D696 |
| -- | 2.0E-4 | cm/cm/°C | ISO 11359-2 |
| Specific Heat (23°C) | 1840 to 2010 | J/kg/°C | ASTM C351 |
| Thermal Conductivity (23°C) | 0.39 to 0.41 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+3 to 2.5E+13 | ohms | ASTM D257 |
| -- | 1.0E+6 to 2.5E+12 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 1.0E+6 to 1.0E+15 | ohms·cm | ASTM D257 |
| 23°C | 9.8E+13 to 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 14 to 91 | kV/mm | ASTM D149 |
| 23°C | 45 to 46 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 2.28 to 3.00 | ASTM D150 | |
| 23°C | 2.55 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | -2.0E-3 to 3.9E-3 | ASTM D150 | |
| 23°C | 3.7E-4 to 1.0E-3 | IEC 60250 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2934-60 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NEXUS Reprocessed PPC 10/2 RBK | Nexus Resin Group, LLC. | PP Copolymer | NEXUS Reprocessed |
| Baydur® 426 IMR (Continuous Filament Mat) | Covestro - PUR | PUR-MDI | Baydur® |
| Hangzhou Plastic PS/PVDC/PE | Hangzhou Plastic Industry Co., Ltd. | Film, PS/PVDC/PE | Hangzhou Plastic |
| LNP™ LUBRICOMP™ WX07423H compound | SABIC Innovative Plastics | PBT | LNP™ LUBRICOMP™ |