| ASTAMID™ KB3EG5 is a flame retardant, low smoke, 25% glass fibre filled Polyamide 6 (PA6) designed for use in applications where a UL94 V-0 flammability rating and high modulus are required. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.52 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 | -- | % | ASTM D955 |
| Water Absorption (24 hr) | 0.40 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (M-Scale) | 119 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 8250 | 5250 | MPa | ASTM D638 |
| Tensile Strength 2(3.20 mm) | 115 | 65.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 3.20 mm) | 2.5 | 4.0 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 7750 | 3750 | MPa | ASTM D790 |
| Flexural Strength 5(3.20 mm) | 170 | 90.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 80 | 120 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 190 | 140 | °C | ASTM D648 |
| CLTE - Flow | 6.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | V-0 | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 210 to 230 | °C | |
| Middle Temperature | 220 to 240 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Pressure | 60.0 to 130 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 5.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC9CSN (Series: CS) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Next Nylon 6 Prime Series NG40-01BK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| Allen ABS 556/499 | SEKISUI Polymer Innovations, LLC | ABS | Allen ABS |
| Carbotex K-40MRA | Kotec Corporation | PC | Carbotex |
| PETLIN LD C150Y | PETLIN (MALAYSIA) SDN BHD | LDPE | PETLIN |