Petrothene® NA143063
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oEk9oz_Petrothene-NA143063.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PETROTHENE NA143 is a series of homopolymer resins for blown film. Applications include stiff liners. NA143 exhibits good processability and clarity. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 1.91 mm) | 11.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 650 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| secant modulus | ASTM E111 | ||
| 1% secant, MD : 32 µm, blown film | 193 | MPa | ASTM E111 |
| 1% secant, TD : 32 µm, blown film | 221 | MPa | ASTM E111 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 32 µm, blown film | 23.4 | MPa | ASTM D882 |
| TD : Yield, 32 µm, blown film | 17.2 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 32 µm, blown film | 300 | % | ASTM D882 |
| TD : Broken, 32 µm, blown film | 500 | % | ASTM D882 |
| Dart Drop Impact (32 µm, Blown Film) | 90 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 32 µm, blown film | 380 | g | ASTM D1922 |
| TD : 32 µm, blown film | 200 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 93.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 31.8 µm, Blown Film) | 70 | ASTM D2457 | |
| Haze (31.8 µm, Blown Film) | 6.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Film data obtained from film produced on a 3½" (89 mm) blown film line, commercially available 8" (203 mm) die, 375°F (191°C) melt extrusion temperature, 2:1 BUR, 1.25 mil (32 micron) gauge, 0.025" die gap at 130 lb/hr. |
| Note Message | |
|---|---|
| 1 . | Type 4, 510mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravamid® BGF20 BK | Ravago Group | Nylon 6 | Ravamid® |
| Ultraform® W 2320 003 BK120 Q600 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Edgetek™ AS-000/000 AS UV | PolyOne Corporation | ABS | Edgetek™ |
| Karina BLUE COLOR CONCENTRATE 06/846-FC-LMP (SDB) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 20-8254 | Lehmann & Voss & Co. | PPA | LUVOCOM® |