Hylex® P1310FR
| Category: | PC , Polycarbonate |
| Manufacturer: | Entec Polymers |
| Trademark: | Hylex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oEequ4_Hylex-P1310FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced, UV Stabilized, UL V-0 Rated |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.14 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 66.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 120 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2140 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 143 | °C | |
| 1.8 MPa, Unannealed | 135 | °C | |
| Vicat Softening Temperature | 152 | °C | ASTM D1525 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.18 mm, in Air) | 15 | kV/mm | ASTM D149 |
| Arc Resistance | 90.0 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 1(1.55 mm, Min. Tested Thickness) | V-0 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.585 | ASTM D542 | |
| Transmittance (3180 µm) | 87.0 to 89.0 | % | ASTM D1003 |
| Haze (3180 µm) | 0.90 to 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | File Number E141008 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOREN PH 21 B 70 | SILON s.ro | PP Homopolymer | TABOREN |
| Ultramid® 8253 HS BK-102 | BASF Corporation | Nylon 6 | Ultramid® |
| Galloo GP-PE-0320 | Galloo Plastics | PE, Unspecified | Galloo |
| Karina RED PVC COMPOUND 813D42/46-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Moplen HP3065 | LyondellBasell Industries | PP Homopolymer | Moplen |