Halene H HD T6
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Haldia Petrochemicals Ltd. |
| Trademark: | Halene H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oEcPZ5_Halene-H-HD-T6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HD T6 is a general-purpose extrusion & lamination film HDPE produced by the Mitsui CX Technology. HD T6 can be used for Lamination films, Woven sacks and Tarpaulin. This grade is characterized by good processability and mechanical strength. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.961 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 28.0 | MPa | ASTM D638 |
| Fracture, molding 2 | 38.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | > 1000 | % | ASTM D638 |
| Flexural Modulus (Compression Molded) | 1100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Compression Molded) | 250 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 131 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 200 - 240 | °C | |
| Cylinder Zone 2 Temp. | 200 - 240 | °C | |
| Cylinder Zone 3 Temp. | 200 - 240 | °C | |
| Cylinder Zone 4 Temp. | 200 - 240 | °C | |
| Cylinder Zone 5 Temp. | 200 - 240 | °C | |
| Die Temperature | 220 - 240 | °C |
| Extrusion instructions |
|---|
| Quench Temperature: 25°C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 4850 | Colorite Polymers | PVC, Unspecified | Unichem |
| Boda BDF601P | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| OTECH ALLOY OE8522 - Profile | OTECH Corporation | TP, Unspecified | OTECH ALLOY |
| 3M™ Dyneon™ PTFE Compound TF 6103N | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| LNP™ THERMOCOMP™ PF008 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |