Borealis PP MB350WG
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | oDhE1R_Borealis-PP-MB350WG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MB350WG is a 30% mineral filled polypropylene compound intended for injection moulding. This material has a very high impact strength while maintaining good stiffness and is easy to process. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 2.5 | g/10 min | ISO 1133 |
| 230°C/5.0 kg | 11 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.90 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 71.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2950 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 29.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 5.4 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 3100 | MPa | ISO 178 |
| Flexural Stress | 45.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 1.5 | kJ/m² | ISO 179/1eA |
| 23°C | 4.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 17 | kJ/m² | ISO 179/1eU |
| 23°C | 55 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 122 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 68.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ISO 306/A50 |
| -- | 83.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 40.0 - 80.0 | °C | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Back pressure: Low to mediumScrew speed: Low to mediumFlow front speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ResMart Ultra TPU 90A ES | ResMart | TPU-Polyester | ResMart Ultra |
| Next Nylon 66 Prime Series PGF25-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Epoxies, Ect. 10-3020 | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| Hifax TYC 1168P | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| OTECH ALLOY OTO9150LSZH - Riser Insulation | OTECH Corporation | TP, Unspecified | OTECH ALLOY |